75104Re: [metalshapers] I need some suggestions.
- Nov 18, 2013Is there such a thing as making this in 2 parts ? front and sides.......you could water jet cut the front....then make the sides to match and bolt the sides to the front...water jet cut the front with enough extra to roll over the parton 3 sides.........same for the cides then bolt -screw the sides to the front....frame would pe zink plated...powder coatet first ....In a message dated 11/18/2013 8:07:57 A.M. Central Standard Time, adveniam@... writes:
On 11/17/2013 8:03 PM, bl55303@... wrote:
> Do you know how to tig weld copper.........sounds like you could
> fab the part and weld it together.
> How many do we need? Could water jet cut the big sides and
> use a tiping wheel to turn the sides.If you can have a 1/4
> flange tiped side you could make a hamerform and do the
> comlpleat letter. Then soder the sides to your letter....A picture
> of what you are trying ti reproduce would be helpful...... Barry L
My initial impulse IS to fab it up. This is tedious , but practical
This curve is just a bit above eye level in a formal greenhouse attached
to a 1920 mansion. Everything done on the place so far is with an eye to
maintaining the visual integrity of the building. The old piece was a
one piece item. The owner knows this. If possible I'd like to follow suite.
The dimensions are still up in the air.
The old one is about 3 inches wide and 2 high.
The new skeletal structure is still being drawn up . I need to cover
that so that it will look as if it is original.
I have told them that I can not even come up with a final design until
the structure is in place.
Working from concept right now I can get some technique figured out.
From plans I can refine the technique and get a good idea about
materials. Given the vagaries of construction actual measurements will
wait until I see the finished project. I did tell them that the closer
they are to perfectly square joints and tolerances of 1/16th inch
dimensionally the less it will cost to clad.
There are a few thousand pieces total If I can deal with it as 20-30
types of pieces rather than all "one of" pieces things will be much better.
I know this can be done, as it was on the old one.
After 45 years or so doing this type of thing, this one will raise the
learning curve for me.
The methods and bench tools used originally probably no longer exist, so
there will be some wheels reinvented possibly.
Introduce yourselves here:
We now have the MSA Forums working. The forums will store our images and will not be erased. The moderators of MSA would like for all "keeper" posts with good technical information and photos, be placed in the forums at the MSA web site:
The forum messages are also forwarded to this email group so you can get them all emailed to you.
Information about copyright policy for materials posted to this group can be found here: http://metalshapers.org/?page_id=11
For those who do not get individual e-mails (with the images) -- you can still get the images by subscribing to dailies at the following address: http://gaudeteforge.com/mailman/listinfo/shadow_gaudeteforge.com
If you do not wish to receive e-mails but do wish to maintain membership privileges -- simply edit your membership for NO EMAIL at the following link:
Yahoo Groups Links
<*> To visit your group on the web, go to:
<*> Your email settings:
Individual Email | Traditional
<*> To change settings online go to:
(Yahoo! ID required)
<*> To change settings via email:
<*> To unsubscribe from this group, send an email to:
<*> Your use of Yahoo Groups is subject to:
- << Previous post in topic Next post in topic >>