Use the 800-522-1215 and ext 2417. That should get you to Lyell Warren at Temescal. He can help you. Thanks, Fred [Non-text portions of this message have been...
Dear All, Contact Ryan Scatena at Thermo Conductive Bonding. They have a proven elastomer bond that has higher thermal performance than standard indium bonding...
George Wityak
gwityak@...
Dec 1, 2006 6:18 pm
3543
Dear Adil, There are several companies that specialize in bonding sputter targets on to copper backing plates. Can you send me more details on your particular...
Dear Sirs We would like to attract your attention to the following one task and one announcement. The TASK: it is necessary to deposit a thin (possible not...
€ ¢Ð’½Ð¸ÐºÐ¾Ð»Ð°Ð¹ € ...
polimag@...
Dec 1, 2006 6:26 pm
3545
Dear Colleague I am doing different type if PVD coatings. Can any one help in finding the manufacturer who can supply the inductive coupled plasma coating...
Hello, I am trying to do functional TiN coating on Tools. I have tried different procedures but it wear out very quickely. The parameters i used are as follow:...
Sidrabe in Riga, Latvia have a system for coating powders. They have done toll coating on powders for R & D purposes and, I am given to believe, have also...
Charles A Bishop
cabishopconsulting@...
Dec 6, 2006 11:26 pm
3548
Paul do you have a relative, who was in the Navy 50 years ago? Jack ... From: PVD_coatings@yahoogroups.com [mailto:PVD_coatings@yahoogroups.com]On Behalf Of...
Jack Kavanaugh
jkav@...
Dec 9, 2006 10:16 am
3549
Mirza: You must increase the coating temperature up to 400°C. Tools should be cleaned with NaOH and the organic solvent. You don´t need to add Argon, it can...
For a good wear performanceof TiN coatings on tools, it depends on careful deposition procedures, including cleaning(pretreatment of the tools), ion cleaning,...
Dear Mirza, After reading of your recipe for deposition I mean it is reasonable the film to wear very quickly. There are a lot of reasons for it - for example...
Hi does anyone have any experience magnetron sputtering NaCl using RF power. So far here are the parameters that I am running at: Power = 100W (110 foward, 10...
Dear All, Does anyone have any experience magnetron sputtering P2O5 using RF power. As I know, the P2O5 oxide is quickly absorbed moisture in the atmosphere. ...
Dear Mirza Assalam o Alaikum]] Why u r worries about the coating. Your recepe is all right. Just try to give Ti interlayer on tour tools. The tools should be...
Dear Colleagues, Please find attached the call for papers of the Symposium Q on "Protective Coatings and Thin Films - 07" to be held in Strasbourg from May 28...
I have a DC sputter and one gas nozzle pipe around the target. I would like to make blue color glass using Ti target and Ar, O2 gas. Will somebody let me share...
Hello I am facing the following problem with my Ti sublimation pump (filament type). I put fresh filaments and after system bakeout started degassing the...
Hello to everyone, I've been working with Al-N films growht by magnetron sputtering r.f. The FTIR spectra show differents peaks between 450 - 100 cm -1 at ...
Hello Colleagues, Has anybody and experience with arcing or sputtering of iron? Because of its ferromagnetic nature it seems to be very difficult to sustain a ...
Dear MS&T’07 participants, Thank you for lending your time and expertise to the MS&T’07 technical program. The Call for Papers was distributed at...
vigase@...
Dec 14, 2006 2:28 pm
3563
Vinay, Did you bead blast (similar to sand blasting) the inside of the sublimation pump? These layers of Ti can hold a lot of water (which is why you use it to...
Andreas, In my experience, there is a different minimum current required for each metal to sustain the arc. I wonder if you need higher current. Mandar...
Mandar Sunthankar
mandar@...
Dec 17, 2006 3:44 pm
3567
Hi everyone, does anyone know poeple able to realize simple gold pattern onto glass slides (or glass plates)? thank you in advance for suggestions and...
NanoSmat 2007 International Conference on Surfaces, Coatings and Nanostructured Materials http://www.nanosmat.org/ 9-11 July 2007, Algarve-Portugal (NanoSMat)...
Hi, Aside from well known masking,photoresist and etch techniques, there are several different ways to achieve patterns (depending on the accuracy and...
Hi, we have some experience with gold patterning on the glass plate by the firm IMT in Switzerland. See http://www.imtag.ch/1eng/index.htm. They were used the...